| Categories | Refractory Castable Material |
|---|---|
| MOQ: | 5 tons |
| Price: | 200-300USD/T FOB |
| Payment Terms: | T/T, L/C |
| Supply Ability: | 3000 tons per month |
| Delivery Time: | 15-20 working days |
| Packaging Details: | Jumbo bag or as requirements |
| Product name: | Corundum Mullite Wear-Resistant Plastic Materials |
| Application: | Industrial Furnaces |
| Color: | Black |
| Raw material: | High Alumina Bauxite,cement |
| Sample: | Freely |
| Shape: | Powder |
| Company Info. |
| ZHENGZHOU CAIHUA KILN MASONRY INSTALLATION CO.,LTD |
| Verified Supplier |
| View Contact Details |
| Product List |
High-strength wear-resistant plastic refers to a mixture of high-grade refractory materials such as corundum, mullite or silicon carbide, and a binder and an admixture (anti-shrinkage agent, preservative, antifreeze).
The high-strength wear-resistant plastic is a semi-wet mud material. When it is applied, water or aluminum dihydrogen phosphate or other liquid is mixed into a mud material, which is pressed or extruded into a block material having a certain plasticity. When thehammer is hit, the plastic is deformed without cracking or slumping, and the deformedshape can be maintained after the external force is released.
High-strength wear-resistant plastic is divided into
corundum-mullite refractory plastic (GNS-65GMS-75GMS-85)carburized
wear-resistant plastic (TS60TS-70) according to the material.
Medium grade. G stands for corundum, M stands for mullite, T stands
for silicon
carbide, and S stands for plastic. The number after the letter
represents the percentageof the main material.
Items | Corundum-mullite | Silicon carbide | |||
/ | GMS-65 | GMS-75 | GMS-85 | TS-60 | TS-70 |
AL2O3% | 65 | 75 | 85 | -- | -- |
SiC% | -- | -- | -- | 60 | 70 |
Bulk density 110℃×24h (dry) g/cm3 ≥ | 2.5 | 2.7 | 2.8 | 2.4 | 2.6 |
Compressive strength/ MPa 850℃×3h(after firing | 70 | 80 | 90 | 60 | 70 |
Normal wear850℃×3h (after firingcm3≤ | 7 | 6+ | 5 | 6 | 5 |
PLC /% (850℃×3h | -0.4～0 | -0.5～0 | -0.5～0 | -0.5～0 | -0.6～0 |
Thermal shock stability (850℃×3h after firing) time≥ | 30 | 30 | 25 | 35 | 40 |
Plasticity index % | 15～40 | ||||
|
Iron Runner 1450 degree Refractory Castable Material For Blast Furnace
Self Flowing 80% Refractory Castable Material High Refractoriness
0.6g/Cm3 620c Insulating Castable Refractory Cement For Heating Furnace
High Alumina Refractory Castable Material Dense Castable Refractory 1700c
High Strength 42% Insulating Castable Refractory Cement 1660 Degree
42-85% Al2O3 Refractory Castable Material Cement For High Temperature Furnace
High Temperature 1640 Degree Castable Refractory Concrete For Fire Resistant Places
Low Cement High Alumina 65% Refractory Castable Material For High Temperature Kiln
High Strength 65-85% Al2O3 LCC Low Cement Castable 1600 Degree Slag Resistance
65% Monolithic Castable Refractory